100% Biodegradable Raw Material Compostable Granules PLA Pellets

• CAS No.: 55231-08-8
• Formula: Pbat
• EINECS: 55231-08-8
• Material: PLA/Pbat
• Usage: Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Model NO.: Eco-201
• Plastic Forming Method: Blow Molding
• Color: White
• Product Name: 100% Biodegradable Raw Material Compostable Granul
• MOQ: 1ton
• Used for: Patch Handle Shopping Bags
• Type: 100% Biodegradeble Material
• Application: Plastic Bags
• Transport Package: 25kg/Bag
• Specification: 25KG
• Trademark: Ecopoly
• Origin: China
• HS Code: 3907999190
• Production Capacity: 1000ton/Month

Product Description

100% biodegradable raw material compostable granules PLA pellets

Eco 201 is composed of PBAT, developed for the extrusion molding applications. See Table 1 for properties.

Table 1- Typical Material Properties
 

Physical Properties	Result	Test Method
Density (g/cm3)	1.532	ISO 1183-1:2012 Method A
Melt Mass Flow Rate (g/10min)	1.62	ISO 1133-1:2011 Procedure A
Mechanical Properties
Flexural Strength (MPa)	58.9	ISO 178:2010/Amd. 1:2013 Method A
Flexural Modulus (MPa)	2625
Izod Notched Impact Strength (KJ/m2)	5.4	ISO 180:2000/Amd.2:2013
Charpy Notched Impact Strength(KJ/m2)	5.9	ISO 179-1:2010
Tensile Modulus (MPa)	2440	ISO 527-1:2012 & ISO 527-2:2012
Tensile Strength (MPa)	47.6
Nominal Tensile Strain at Break (%)	50.6
Thermal Properties
Heat Deflection Temperature (oC)	52.9	ISO 75-2:2004

Application

 The Eco 201 are developed for the application of bags.

Processing Information

 It can be processed on most conventional extrusion molding equipment. The material is stable in the molten state, provided that the drying procedures are followed. Mold flow is highly dependent on melt and mold temperatures. The extrusion temperature is between 180oC and 200oC. Moreover, the extrusion molding parameters should be adjusted according to the actual circumstance.